Polyurethane-ureas based on cis-trans-1,4-diaminocyclohexane

ABSTRACT

Light stable polyurethane coatings with a considerably increased softening range and melting points coupled with improved resistance to perchlorethylene is obtained by using a chain extender comprising at least 80 mol % 1,4-diamino cyclohexane with a cis/transisomer ratio of from 10/90 to 60/40.

nited States Patent [191 ertel et a1.

POLYURETHANE-UREAS BASED ON ClS-TRANS-l ,4-DIAMINOCYCLOHEXANE Inventors: Harald Oertel, Odenthal-Gloebusch;

Bruno Zorn, Cologne; Wilhelm Thoma, Bergisch-Neukirchen; Klaus Noll, Cologne, all of Germany Bayer Aktiengesellschaft, Leverk'usen Filed: Apr. 23, 1973 Appl. No.: 353,279

Assignee:

Foreign Application Priority Data May 4,1972 Germany 2221798 Cl. 260/33.8 UB, 260/31.8,260/326 N,

260/32.8 R, 260/33.2 R, 260/33.4 UB,

260/33.6 UB, 260/75 Nl-l llnt. Cl C08g 51/28, C08g 22/04 Field of Search. 260/75 NH, 77.5 AM, 75 NK,

Primary ExaminerH. S. Cockeram Attorney, Agent, or Firm-Gene Harsh ABSTRACT Light stable polyurethane coatings with a considerably increased softening range and melting points coupled with improved resistance to per ohlorethylene is obtahied liy using a ohain extender oomph sing at least 80 mol 1,4-diamino cyclohexane with a cis/transisomer ratio of from 10/90 to 60/40.

10 Claims, No Drawings POLYURETHANE-UREAS BASED ON CIS-TRANS-l,d-DlAMlNOCYCLOfiEXANE This invention relates to a process for the production tion of light-stable films and-coatings with high softening ranges from such solutions,

It is known that substantially linear polyurethanes can be obtained from solutions of relatively high molecular weight polyhydroxy compounds such as polyesters, aliphatic or cycloaliphatic diisocyanates such as hexamethylene diisocyanate, dicyclohexyl methane diisocyanate or 1-isocyanato-3-isocyanato methyl-3,5,5- trimethyl cyclohexane, and chain-extending agents such as ethylene diamine, l-amino-3-amino-methyl- 3,5,5-trimethyl cyclohexane or 4,4-dicyclohexyl methane diamine. Highly polar amides such as dimethyl formamide can be used as solvents. Polyurethanes based on l-isocyanato-3-isocyanato methyl-3,5,5- trimethyl cyclohexane and/or 1-amino-3-aminomethyl- 3,5,5-trimethyl cyclohexane, in particular, are also so]- uble in weakly polar solvents such as toluene/isopropanol which simplifies to a very considerable extent the processing of polyurethane solutions such as these into coatings, because high-boiling, physiologically unacceptable solvents such as dimethyl formamide can be avoided.

On account of their synthesis from (cyclo) aliphatic diisocyanates and (cyclo) aliphatic diamine components, polyurethane-ureas of this kind do not discolor on exposure to light and are considerably more stable than comparable polyurethanes based on aromatic diisocyanates such as, for example, diphenylmethane- 4,4'-diisocyanate. Accordingly, they are used with advantage in the production of flexible textile coatings or as surface layers on coatings. Unfortunately, their favorable solubility and light-stability properties are offset by their typically unfavorable property of a relatively low softening range and a relatively low melting point. Thus, polyurethane-ureas of this kind begin to soften at temperatures far below 200C and, in some cases, even at temperatures below 150C, while their melting point (Kofler bench) is generally between 180 and 210C, even in the'case of relatively hard polyurethanesthigh NCO-content in the prepolymer, for example 5.5% by weight). 1n the case of coatings, the

low softening range impairs fastness to rubbing under heat and resistance to hot ironing or behavior in heated presses (forexample, in the case of artificial leather). In addition, coatings of this kind frequently show very high swellability in solvents of the kind used in dry cleaning, such as-perchlorethylene.

It has now surprisingly been found thatlight-stable polyurethane coatings with a considerably increased softening range and melting points, coupled with improved resistance to perchlorethylene, can be obtained by using 1,4-diamino cyclohexane in certain stereoisomeric cis/transmixtures as chain extender which also results in-the polyurethane-ureas formed having out standing resistance to solvents.

The invention therefore relates to a process for the production of stable, light-resistant solutions of polyurethane ureas from prepolymers with terminal isocyanate groups and diamines in weakly polar solvents, distinguished by the fact that prepolymers of a. substantially linear polyhydroxyl compounds with molecular weights of from about 500 to 5000,

b. optionally low molecular weight dihydroxy compounds,

0. and aliphatic or cycloaliphatic diisocyanates, the molar ratio of hydroxyl groups to isocyanate groups being between about 1 1.5 and l 5,

are reacted with diamines as chain extenders in a solvent or mixture of solvents of aromatic which may be chlorinated and/or chlorinated aliphatic hydrocarbons and primary, secondary and/or tertiary aliphatic and/or cycloaliphatic alcohols, at least mol of the chain extender being 1,4-diamino cyclohexane with a cis/- trans-isomer ratio of from 10 to 60 40.

The polymers prepared in accordance with the invention generally melt at temperatures in the range of from 250 to 270C and begin to soften at temperatures of from about 215 to 240C. The thermal properties are accordingly improved by some 50 to 60C by using the chain extenders according to the invention. ln addition, the polyurethanes according to the invention are also extremely fast to light and can be prepared in a highly hydrolysis-stable composition by using dihydroxy polycarbonates based on hexane diol as the relatively high molecular weight polyhydroxyl compounds. It is possible, bythe incorporation of low molecular weight diols containing tertiary amine groups, to obtain a further improvement in light stability beyond the already existing stability level.

Although the use of pure trans-1,4-diamino cyclohexane as chain extender also leads to products of very high melting point, it does involve the disadvantage that the polyurethanes synthesized in this way do not remain stably dissolved in many of the solvent mixtures according to the invention and rapidly change from their solutions into a paste-like, gelled form in which they are no longer suitable for processing into coatings. With pure cis-l,4-diamino cyclohexane the melting point of the polyurethane coatings falls again and approaches the behavior of known polyurethanes based on conventional diamine extenders as described above. A lower softening range is also found with 1,3diamino cyclohexane.

By using a certain cis/trans-mixture of the stereoisomeric 1,4-diamino cyclohexanes in accordance with the invention, it is possible to obtain both a considerably improved softening range and melting range of the polyurethanes and also an adequate level of solubility of these polyurethanes in the moderately polar solvent mixtures of comparatively high volatility that are preferably used.

At the same time, a distinct improvement in light stability is obtained, by comparison with the products obtainable with conventional chain extending agents.

The cis-enriched diamino cyclohexanes are liquid and can readily be separated from the isomer mixture; the trans-compound of the l,4-diamino cyclohexane is crystalline and can be readily recrystallized, for example from petroleum ether, and obtained in pure form. The cis/transratio can be determined by nuclear resonance spectroscopy (220 mc/s apparatus) at 2.836 ppm and 2.597 ppm.

The preferred cis/trans-ratios of the 1,4-diamino cyclohexane are from 50:50 to 15:85, the most favorable range being from about 40:60 to 20:80.

The substantially linear polyurethane ureas are prepared by methods known per se. Substantially linear polyhydroxyl compounds such as dihydroxy polyesters, polycarbonates and polyacetones with molecular weights of from about 500 to 5000 (preferably from 800 to 3000) and melting points below 60C (preferably below 45C) are reacted with the aliphatic and/or cycloaliphatic diisocyanates in an NCO OH molar ratio of from about 1.5 1 to about z 1, preferably from 2: 1 to 3 1, to form the NCO prepolymer. (If the molar ratio is greater than 2 l, the reacted mixture contains fractions of the monomeric diisocyanate in addition to the NCO prepolymer. In the following, the term prepolymer is also intended to cover mixtures of this kind).

Examples of polyesters suitable for the process according to the invention include adipic acid-ethylene glycol, -l,6-hexane diol, -2,2-dimethyl propane diol, -1,4-butane diol or -1,2-propane diol polyesters or mixtures of these components. The adipic acid in the polyesters may also to some extent be replaced, for example, by phthalic acid or isophthalic acid. Polycaprolactone ester types which contain the hydroxy caproic acid unit as a structural component, are particularly suitable because of their resistance to hydrolysis. Dihydroxy polycarbonates based on 1,6-hexane diol or mixed polycarbonates into which adipic acid, for example, is incorporated in small quantities instead of carbonic acid, for example in quantities of about 20 mol are even more suitable because of their outstanding resistance to hydrolysis. Mixtures of the aforementioned compounds can also be used.

In addition to the relatively high molecular weight polyhydroxy compounds, low molecular weight diols with molecular weights of from 62 to about 400. for exampleethylene glycol, 1,4-butane dio1,2,3-butane diol; 2,2-dimethyl-1,3-propane diol or N-stearyl-N,N'-bisoxethyl urea, can also be used in relatively small quan- 1,4-diamino cyclohexane with cis/trans-isomer ratio according to the invention can be used on its own as a chain extender, although it is also possible to use other. preferably amino functional compounds known per se. although their content should preferably not amount to any more than 20 mol of the chain extenders. so that the melting point of the polyurethanes is not excessively reduced. Other chain extenders are preferably added in quantities of up to about 12 mol 7r. for example ethylene diamine, 1.2-propylene diamine. hexa methylene diamine, N-methyl-bis (3-amino propyl)- amine, bis-N,N-(3-amino propyl)-piperazine, 1,3- cyclohexane diamine. 4,4'-dicyclohexyl methane diamine, 3,3-dimethyl-4,4-diamino dicyclohexyl methane and l-amino-3-aminomethyl-3,5,5-trimethyl cyclohexane. Preferred co-extenders include ethylene diamine, dicyclohexyl methane diamine and l-amino-3- aminomethyl-3,5,5-trimethyl cyclohexane.

It is also usually possible to use small quantities of monoamines or amino alcohols for chain termination of the polyaddition reaction and small quantities of triamines to increase viscosity.

In the process according to the invention, the diamines are reacted with the NCO-prepolymers in preferably equivalent or slightly excess quantities (for example in NH NCO molar ratios of 1 1 to 1.15 1). Due to the avoidance of an excess of NCO, solutions of this kind are highly stable on storage. The free amino groups can also be reacted with diisocyanates and polyisocyanates in, at most, equivalent quantities (accompanied by an increase in viscosity) or with monoisocyanates (to remove terminal amino groups).

The polyurethanes which can be obtained by the process according to the invention contain typical (hard segments (of diisocyanate and diamines) with the structure:

'{CO.NH-D-NH. co. (NH- eis/trans) tities (about 0.05 to 1 mol per kg of elastomer) in the preparation of the prepolymer. Diols containing tertiary amino groups, for example N,N-bis-(B-hydroxyethyl)-methylamine, N,N-bis-(,B-hydroxy ethyl)- isopropyl amine, N,N-bis-(,B-hydroxy propyl)-tert.- amylamine and bis-(3-aminopropy1)-piperazine, are

particularly preferred because, in this way, a considerable further improvement in stability against loss of strength under theeffect of light is obtained in the already light-stable non-discoloring polyurethanes. Other diol compounds containing tertiary amino groups suitable for use in. the process according to the invention are describedin German Offenlegungsschrifts Nos. 1,495,830 and 2,058,502.

The preferred isocyanate component is l-isocyanato- 3-isocyanato methyl-3,5,5-trimethyl cyclohexane, which may be mixed with smaller quantities (of up to about 25 mol of other aliphatic or cylcoaliphatic diisocyanates. for example hexamethylene-l,6- diisocyanate; 2,2 ,4-trimethyl hexane-l,6-diisocyanate; 4,8-dioxa-6,6-dimethyl undecane-1,ll-diisocyanatej lysine-C -C -alkyl ester diisocyanates; 1,4- dicyclohexane diisocyanate and, in particular, 4,4- dicyclohexyl methane diisocyanate or 3,3'-dimethyl- 4,4'-dicyclohexyl methane diisocyanate (preferably in the form of the cis/cisor cis/trans-enriched stereoisomer mixtures).

in which the groups D are pfedominantly radicals of the formula and x is an integer of from 1 to 5. In addition, D can also be a radical of a (cyclo)aliphatic diisocyanate, for example the hexamethylene radical or the dicyclohexylmethane radical Structures containing the radical cess according to the invention. The l,4-diamino cyclohexane radical NI-I E I-NH- I the light stability of polyurethanes such as there is low in the absence of specific stabilization.

In addition to the hard segment structures, the incorporation of low molecular weight dihydroxy compounds into the prepolymer alsogives rise to the forma tion of structural segments such as which are attached to the relatively high molecular weight dihydroxy compounds through urethane groups and/or to the hard segments through urea groups. G is the radical of the low molecular weight dihydroxy compound, for example an alkylene or cycloalkylene radical with up to l3 carbon atoms and, preferably, an N-alkyl-(alkyleneh-radical in which the primary, secondary or tertiary alkyl group contains from 1 to 12 carbon atoms and the alkylene groups contain from 4 to carbon atoms.

Solvent mixtures of aromatic or aliphatic hydrocarbons which may be chlorinated with primary, secondary and/or'tertiary aliphatic and/or cycloaliphatic alcohols, are particularly suitable for use as solvents for the substantially linear, aliphatic polyurethane-ureas with the aforementioned structures and for the process according to the invention. The solutions have solids contents of from about 5 to 40% by weight, preferably from to 35% by weight. Examples of the hydrocarbons used in the process according to the invention include toluene, xylene, ethyl benzene, mesitylene, chlorotoluenes and hydrocarbon cuts of petroleum or synthesis fractions predominantly containing aromatic hydrocarbons (for example Essos Solvesso-IOO of hp. l56l78C., flashpoint 45 C). Compounds such as trichloroethylene orperchlorethylene are used as the chlorinated aliphatic hydrocarbons while preferred alcohols include C -C alcohols such as ethanol, propanol, isopropanol, butanol, isobutanol, primary, secondary, or tertiary amyl alcohols, primary, secondary or tertiary hexyl alcohols, tert.-butanol or ter.-octyl alcohol, and also diacetone alcohol. Mixtures of toluene or xylene with isopropanol, isobutanol or tert.-butanol are particularly effective solvents. The solvent mixtures (in hydrocarbon :alcohol quantitative ratios ofl 10 to l0 l,preferably from l 3 to 3 l) have better dissolving properties than the individual components. Relatively high boiling solvent mixtures such as Solvesso/ethylene glycol monomethyl ether or Solvesso/ethylene glycol monoethyl ether have the advantage of giving the solution a higher flashpoint although, on the other hand,

they are more difficult to remove again than the readily volatile solvents during the further processing of the polymer solutions.

Other solvents may be added as diluents to the solutions before processing, for example before spraying of the solutions, in order to obtain the low viscosity required. On the other hand, any required film-forming rate can be adjusted by additions of high-boiling solvents. Examples of such solvents include mcthylcne chloride, tetrahydrofuran, dioxan, ethyl acetate, methyl ethyl ketone, amyl acetate or, as high-boiling solvents, ethylene glycol monomethyl ether acetate or even dimethyl formamide in small quantities.

Such additives as stabilizers, anti-agers, hydrolysis stabilizers, UV-absorbers, soluble dyes, pigments of organic or inorganic structure, fillers, carbon black or white pigments can be added in the usual form and quantities of the polyurethane solutions as known per se for modification purposes. Whiteners or other soluble high molecular weight substances, such as nitrocellulose, cellulose esters and ethers and other derivatives, also soluble polymers or polycondensates, can also be added.

Application of the polyurethane urea solution mixtures for layer formation to substrates or intermediate supports is carried out by any process known per se, for example by casting, doctor-coating spread-coating, brush-coating, spray-coating or printing. Textile coatings on, for example, webs, woven fabrics or knitted fabrics can be applied in relatively thick layers in the case of relatively soft polyurethane settings (softness controlled by the NCO-content of the prepolymer used for preparation; for example 2.5 to 4.5% by weight of NCO) in any constructions and aftertreatment stages (for example roughened surfaces). The solution mixtures can also be applied to intermediate supports, for example release papers, steel bands or siliconized fabrics, in which case the films formed can be further processed by bonding or by the reversal process.

In one preferred procedure, roughened cotton fabric weighing approximately 220 to 240 g/cm is coated with the polyurethane solution by the reversal process on a coating machine by means of doctor rolls. To this end, a surface layer is applied with the solution to the release paper and dried in a first operation through the drying ducts of the coating machine at temperatures rising from to C. The coating is applied in a quantity of from about 40 to 50 g/cm of solid substance. In a second operation, the elastomer solutions are diluted with approximately 5 to 10% of dimethyl formamide or cyclohexanone and are applied as an adhesive coat to the dry surface layer, the fabric is laminated on and the web dried again in the drying duct. The release paper andzthe laminated fabric are separately wound up after leaving the drying duct. The total application of polyurethane to the fabric amounts to between about 60 and 90 g/cm. Approximately 10 to 20% of pigments can be incorporated in the solutions in order to provide them with any required color.

Harder polyurethane settings (NCO-contents of from about 4 to 7% by weight in the prepolymer) are preferably applied as surface coats or as finished to textile coatings, leather or artificial leather, for example by doctor-coating, spray-coating or printing, and the solvent is removed by brief heating, for example by heating for. 3 minutes at C.

The invention is further illustrated but is not intended to be limited by the following examples in which all parts and percentages are by weight unless otherwise specified.

EXAMPLE 1 NCO-prepolymer formation 1200 parts of a 1,6-hexane diol polycarbonate with an OH number of 58.25 (molecular weight 1925) are stirred with 25.7 parts of N,N-bis-(B-hydroxy prpyl)- methyl amine, a solution of 405.8 parts of lisocyanato-3-isocyanato methyl-3,5,5-trimethyl cyclohexane in 408 parts of Solvesso-lOO (aromatic solvent cut with a flashpoint above 45C, an Esso product) is added at65C and the 80% solution is subsequently heated for 2 hours to 95C for prepolymer formation. The prepolymer has an NCO content of 5.28% (calculated on solid substance).

a. Chain extension with 1,4-diamino cyclohexane (36% cis/64% trans-ratios) 9.25 parts of 1,4-diamino cyclohexane are dissolved in 371 parts of an ethylene glycol monoethyl ether/Solvesso-100 mixture (1 1 parts by weight) and 155.5 parts of prepolymer solution introduced in the form of a thin stream with vigorous stirring (102 equivalents of NH to-100 equivalents of NCO). The homogeneous highly viscous 25% solution formed has a solution viscosity of 1050 poises/20C. Theproperties of films cast from this solution (doctor-coating on to glass plates, followed by evaporation of the solvent at about 70 to 100C) are shown in Table l.

The solution shows outstanding levelling behavior, even after standing for several weeks.

A finish prepared from the solution on sheets of artificial leather is surprisingly resistant to aqueous-alcohol mixtures, in contrast to polyurethanes which have been chain extended for example with ethylene diamine or l-amino-3-aminomethyl-3,5,5-trimethyl cyclohexane (see comparison tests). However, the substance is readily soluble in the solvent mixture used for production and in mixtures of toluene and isopropanol.

In order to test the properties of the finish, 100 parts of the 25% FUR-solution (dissolved in a mixture of S01- vesso-100 and ethylene glycol in a ratio of l 1) are diluted with 50 parts ofa solvent mixture of 50% of ethylene glycol, 25% of toluene and 25% of isopropanol and applied with a doctor knife in a layer thickness of 12 p. to a knitted fabric which has been coated with polyurethane by the reversal process. After drying for 1 minute at 140C and cooling, the finished material is dry, has a very fine gloss coupled with a pleasant feel and shows favorable fastness to rubbing and flexing:

300 rub-strokes under a load of 1 kp with a VESLIC apparatus (according to Schweize Farbechtheitsprufungsblatt C 4500);

over 100,000 flexings according to DIN 53 340.

The finish is resistant to rubbing with 50% alcohol, it shows very moderate resistance to 98% alcohol. lts fastness to light, as measured on the 8-stage international blue scale, is greater than 7. After storage for 4 weeks at 70C/98% relative humidity, a film prepared from the polyurethane solution still has 94% of its original ultimate tensile strength which is outstanding for polyester polyurethanes. 100 parts of the lacquer of Example 10, but prepared in a mixture of tert.-butanol and xylene (l 1), are dissolved in 300 parts ofa mixture of equal parts-of ethyl glycol, dimethyl formamide and toluene and colored with a standard light-brown nitrocellulose pigment (Bayers Egaloncaramel). This solution is sprayed on to the embossed surface of an artificial leather (5 to 6 g of dry substance per m The artificial leather consists of a latex-bonded polyamide fiber web with a surface layer of coagulated polyurethane (approximately 0.3 mm thick). After spraying and drying ofthe finish, the unpleasant rubber-like feel has completely disappeared. The surface shows a fine gloss, coupledwith high resistance to flexing, scratching and rubbing. The resistance of the finish to aliphatic hydrocarbons is extremely good and its resistance to concentrated alcohol is moderate.

b. Comparison test Chain extension diaminocyclohexane The trans-1,4-diamino cyclohexane is obtained by treating the semi-solid cis/trans-mixture of (a) with petroleum ether, filtering off the solid fraction under suction and recrystallizing the solid isomer from petrol with a melting point of 65 to 67C and a trans-isomer content of 97%.

9.25 parts of the trans-isomer of 1,4-diamino cyclohexane are reacted with 155.5 parts of the prepolymer solution of 1(a) (102 equivalents of NH to 100 equivalents of NCO). A homogeneous, highly viscous 25% solution is obtained, becoming steadily more viscous in a matter of minutes so that it is diluted with 132 parts of a Solvesso/ethylene glycol mixture to a solids content of 20%. The solution then has a viscosity of around 1500 poises and changes into a totally gelled form (crumbly without any flow properties) over another 30 minutes at room temperature. A coating is applied from the paste, the solvent evaporated off and the 11,-- value measured in hexamethyl phosphoramide. The 11,- value of 0.85 corresponds to a conventional highpolymeric linear polyurethane elastomer. Accordingly, gelling is by no means attributable to crosslinking, but merely to an increase in viscosity. The substance has an extremely high softening point and melting point (see Table 1), but in this composition is neither solvatable nor soluble in the aforementioned solvents, but only in highly polar solvents such as dimethyl formamide.

c. Comparison test Chain extension with cis-enriched 1,4-diamino cyclohexane cis/25% trans) The sample is obtained by decanting off the liquid fractions from the stereoisomer mixture of diamino cyclohexane which is semi-solid at room temperature and, according to NMR-analyzing, contains 74.8% of cisand 25.2% of trans-isomers.

9.25 parts of the cis-enriched 1,4-diamino cyclohexane are reacted with 155.5 parts of the prepolymer solution of 1 (a) to form a homogeneous, highly viscous 25% solution and diluted to a solids content of 20.4%. After 1 day, this solution has lost its homogeneity and flow properties and, after 2 days, has changed into a paste-like form. Some of the solution was diluted to 15% immediately after preparation and cast into films (see Table 1). The softening point is distinctly lower than in test 1 a.

(1. Chain extension with a mixture of cis-enriched and trans-1,4-di'amino cyclohexane Equal parts of the trans-isomer used in 1 (b) (97% trans/3% cis) and the cis-mixture used in l (c) (74.8% cis/25.2% trans) are used for chain extension, giving a with trans-1,4-

mixture with a trans-isomer content of 61 .6% and a cisisomer content of 38.4%. n V

9.25 parts of the (38.4% cis/6l.6% trans)-1,4- diamino cyclohexane are reacted as in 1 (a) with 155.5

69.3 parts of 1,4-diamino cyclohexane (17.3% cis/82.7% trans) are dissolved in 2411 parts of toluene/isopropanol (1 l) and 1200 g of the above NCO prepolymer solution (the equivalent quantity) A prepolymer solution is prepared in accordance with Example 1. the only difference being that toluene is used as the solvent. instead of Solvesso-lOO. The prepolymer solution obtained has an NCO-content of 5.32%. based on solids. The chain-extending reactions are carried out in toluene/isopropanol (ratio by weight 1 l).

a. Chain extension with 1,4-diamino cyclohexane (82.7% trans/17.3% cis) parts of prepolymer solution, resulting in the formation stirred The homogeneous solution has a viscosity of of a homogeneous, highly viscous and stable elastomer 680 P f" ObSeFVaUO'n'PeTIQd 0f 1 t lhc solution. Following dilution of part of the solution, solution was g- The film properties are films are prepared and their properties determined (see Show" In Table The techmcill propertles as fmlsh Table 1). The technical properties correspond to those correspond to the values glven ln Example la. lf toluf E l 1 A V ene is replaced by chlorobenzene, homogeneous stormp' fi I age-stable elastomer solutions are also obtained, from Chain extension with ethylene diamine which finishes with the properties and characteristics 3.25 parts of ethylene diamine in 230 parts of Solvesg'ven m EXamPle 1 f can P P so/ethyl glycol (l 1 l) are mixed with stirring with 1075 f e Wlth 1,4-d1amm0 cycl hexane/ethyparts of the NCO-prepolymer solution (equivalent lene damme (90 I 9 quantity), resulting in the formation of a clear homoge- Parts of the I'4'dIammO cyFlollexane m 2 neous solution with a viscosity of 286 poises at 20C (c f' Parts of 98% Fthylene dlamme are dlssolved 26.6%). The solution remains stable over several parts of ioluenfilfiopmpanol 3 l) and surfed weeks. Films cast from the solution show the properties a substamlany equwalem quanmy h Q' Set out in Table 20 prepolymer to form a homogeneous solutlon wlth a vls- Th w a Soft of these elasto cosity of 270 poises at 20C and a solids content of e s e g p The solution remains stable over the observation l i, l f lna... period of 1 month; the properties of the films are set On exposure to llght, the fllms are far less stable to out in Table The high melting point of 2a remains dehydratlon than films prepared according to Example 25 Substantially unahere la although nelther of thetwo fllms dlscolors under co extension with LLdiamino cyclohexane/why s lote t Q ...F .9 PE I$PFQP QP$: lene diamine so 1 20) The coatings soften very considerably when treated In the event of similar extension with 20 mol f with aICOh 0t ate /a co I and are s i u y ethylene diamine as co-extender (4.62 parts of diamino damaged by even gentle rubbing. This behavior is also cyclohexane/0.62 parts of ethylene diamine), a homoshown by coatings of polyurethanes prepared with lgeneous storage-stable solution with a viscosity of 270 amino-3-aminomethyl-3,5,5-trimethyl cyclohexane inpoises/20C and a solids content of 25% is also obad f tht sn qianinsi- Table 1 Solution and film properties of polyurethane ureas according to Example 1 Example 1,4-diaminocyclo solution Solution 17 i-value hexane viscosity concentration cis/trans content (7:) poises/20C ('72 by'weighi) l a) 36/64% 1050 25 0.76 lb) 3/97% 1500 20 0.85

(comparison test (very quickly gelled) l c) /25 2000 20.4 0.88

(comparison test) 1d) 38.4/61.6 q 2500 20.5 0.96 l e) ethylene diamine 286 26.2

(comparison test) Example Ultimate Breaking Heat distortion Melting behavior Remarks tensile elongation temperature Kofler bench strength ('7!) HDT: (cf. DOS softening melting point g/dtex 1770591) c "C l a) 0.74 447 143.5 235C 26U"C Solution stable almost liquid 1 b) cannot be no film approx. 260C) solution unstable,

measured 260C turning immediately into a paste 1 c) 0.84 471 l24 2l5-220 239 solution unstable.

' turning into a paste after standing for 1 day l d) 0.80 481 154 230-245 260 liquid solution stable 1 e) 0.83 442 103 l75l93 205 liquid film damaged when rubbed with ethanol EXAMPLE 2 60 d. Co-extension of 1,4-diamino cyclohexane with lamino-3-aminomethyl-3,5,S-trimethyl cyclohexane l 0) 1f 10 mol of 1-amino-3-aminomethyl-3,5,5- trimethyl cyclohexane areused instead of the ethylene diamine (5.18 parts of 1,4-diamino cyclohexane according to 2a/0.86 parts of l-amino-B-aminomethyl- 3,5,5-trimethyl cyclohexane), with the procedure oth-- erwise the same as in Example 2b, a storage-stable homogeneous elastomer solution with a viscosity of 380 ,given in Table 2.

Table 2 Films of this solution show a melting point of 260C. softening beforehand at temperatures upwards ofabout 225 to 235C. Softening is somewhat more pronounced than in Example 1 because the urethane has a softer" structure (less NCO, i.e. less hard segment). v,-value 0.70 (see Table 3).

Chain extension can also be carried out in ,toluene/isopropanol and xylene/tert.-butanol mixtures (3 lto l 3), stable solutions again being obtained.

Solution and film properties of the polyurethane ureas according to Example 2 1,4-diamino cyclo 600 parts of the hexane diol polycarbonate of Example 1 are heated for some 220 minutes to 97C with 138.5 parts of 1-isocyanato-3-isocyanato methyl-3,5,5- trimethyl cyclohexane and 185.5 parts of Solvesso-l00,

' resulting in the formation of a prepolymer solution with ring. A homogeneous, storage-stable solution with a 50 Example solution solution 1; i-value hexane viscosity concentration cis/trans content poises/ 17.3/82.7Z C

2 a) 100% 680 28 0.85 2 b) 90% 1.4-diamino 270 cyclohexane 10% ethylene diamine 2 c) 1,4-diamino 270 25 0.84

cyclohexane 20% ethylene diamine 2 d) 1,4-diamino 380 25 0.85

cyclohexane 10% l-amino-3- aminomethyl-3.5,5-' trimethyl cyclohexane 2 e) 90% 1,4-diamino, 220 25 0.82

cyclohexane l0% l, 3 tlia r n ing 2-. ...H cyclohexane Example Ultimate Breaking HDT determined melting behavior tensile elongation in accordance Kofler bench strength with DOS 1770591 softening melting point g/dtex (C) (liquid) C -2 a) 0.76 434 157 240 265 2 b) 0.73 425 14-7 235 255 2 c) 0.76 400 144 225 250 2 d) 0.80 443 153 (220-1240 260 2 e) 0.79 407 152 (215 )240 264 EXAMPLE 3 b. Comparison test Chain extension with ethylene diamine and with 1-amino-3-aminomethyl-3,5,5-trimethyl cyclo- Elastomer solutions are prepared and cast into films in the same way as in test 3a, but with 2.25 parts of ethylene diamine (a) and 6.25 parts of 1-amino-3- amin omethyl-3,5,5-trirnethyl cyclohexane (B).

These polyurethane films have a much lower melting point: with ethylene diamine, 203C, softening considerably before melting at above 152C, with l-amin0-3- aminomethyl-3,5,S-trimethyl cyclohexane 214C, softening before melting at above 178C. In addition, a distinct reduction in strength on exposure to light is also observed (see Table 3).

Table 3 Example Exposure Ultimate tensile Breaking elongation Modulus 300% No. Time strength g/dtex 7r mg/dtex 3 a) original 0.69 487 219 66 hours 0.57 445 210 hours 0.50 474 188 154 hours 0.25 360 163 3 b/a original 0.64 450 168 (ethylene diamine) 66 hours 0.22 452 87 110 hours 0.17 422 79 154 hours cannot be measured original 0 450 254 (l-amino-B- uminomethyl- 66 hours 0.57 457 223 3,5,5-trimethyl cyclohexane) 110 hours 0.29 382 1112 154 hours 0.15 327 112 EXAMPLE4 1500 parts of an adipic acid/1,6-hexane intensively stirred with 1073 parts 'of prepolymer-solution. After dilution of the highly viscous solution to 25%, the homogeneous elastomer solution has a viscosity of 390 poises/20C.

The films show favorable mechanical properties, a melting point of 260C and a softening range of from about 222 to 235C.

After the solution has been cast to form a reversal film, the following properties were measured on the clear, tack-free film: shore hardness 86, ultimate tensile strength 600 kg/cm breaking elongation 580%; ultimate tensile strength after 66 hours Fade-o-meter testing 290 kg/cm elongation 670%; after 400 hours Fade-o-meter testing 250 kg/cm 660% elongation. After hydrolysis for 7 days at 70C/95% relative humidity, the films have a residual strength of 540 kg/cm at 470% elongation which, after 14 days falls to 410 kg/cm at 620% elongation.

EXAMPLE 800 parts of a hexane diol polycarbonate of molecular weight 1925, 15.78 parts of N,N-bis-(B- hydroxy propyl)-methyl amine, 208.8 parts of 1-isocyanato-3- isocyanato methyl-3,5,5-trimethyl ,cyclohexane and 257 parts of toluene, are heated to 110 115C until the NCO content of the prepolymer solution has fallen to3.365% NCO (based on solid substance). 36.6 parts of 1,4-diamino cyclohexane (30% cis/70% trans) are mixed with 1958 parts of toluene/isopropanol (l 1) and 1000 parts of the above NCO-prepolymer solution, resulting in the formation of a homogeneous, storagestableclear elastomer solution. The film begins to soften fairly considerably at around 220C and becomes liquid above 260C. The film properties are 7 the following data (accompanied for comparison by the data of a comparison substance of similar compositipn extended with l-amino-3-amino methyl-3,5,5-trimethyl' cyclohexane):

Example 5 Comparison micro hardness 82 84 ultimate tensile strength kg/cm 570 480 breaking elongation 370 340 7 days hydrolysis at 70C/95 relative (strength/elongation) humidity 525/390 450/420 14 days hydrolysis under the same conditions I 510/380 440/380 400 hours Xeno- (strength/elongation) testing 470/410 315/380 swelling in perchlorethylene The solutions of Example 5 give high-strength, hydrolysis-resistant and light stable polyurethane coatings which show extremely low swelling and, hence, high dry-cleaning resistance.

EXAMPLE 6 720parts of the hexane diol polycarbonate used in Example-l and 80 parts of an adipic acid-1,6-hexane diol/2,2-dimethyl-1,3-propane diol polyester with the same composition as in Example 4, are heated for 160 minutes to between 95 and 98C with 194.5 parts of lisocyanato-3-isocyanato methyl-3,5,5-trimethyl cyclohexane and 57 parts of dicyclohexyl methane-4,4- diisocyanate (molar ratio of the diisocyanate 20) in 265 parts of toluene, resulting in the formation of an NCO-prepolymer with an NCO content of 5.44%

(based on the solids content).

13.45 parts of 1,4-diamino cyclohexane (36/64 cis/- trans-mixture) and 4.48 parts of dicyclohexyl methane- 4,4'-diamine (97.7%.) [molar ratio of the diamines 15] are dissolved in,604parts of toluene/isopropanol l/l and 259 parts of the above NCO prepolymer solution added, resulting in the formation of a highly viscous elastomer solution (860 poises) which, after diluamine or l-amino-3-amino methyl-3,5,5-trimethyl cyclohexane, much lower-melting films are obtained.

If it is attempted to synthesize an NCO-prepolymer solution from a mixture of 50/50 mol of lisocyanato-3-isocyanato methyl-3,5,5-trimethyl cyclohexane/dicyclohexyl methane diisocyanate, and if the solution in toluene/isopropanol is chain-extended as above with 1,4-diamino cyclohexane, an unstable solution is obtained which very quickly turns into a paste and can no longer be spread.

this 4 Solution and film properties of the polyurethane ureas according to Examples 3 to 6 ("softer" coating type approximately 3.5% of NCO in the prepolymer) Example 1.4-diamino solution viscosity solution m-value v cyclohexane cis/ poises/20C concentration trans content '3 a) 17.3 82.7 266 -2s.2 0.70 3 b) comparison tests with ethylene diam'ine 26.2 l-amino3-amino 26.2 methyl-3,5,5-

trimethyl cyclohexane TABLE 4 Continued Solution and film properties of the polyurethane ureas according to Examples 3 to 6 (softer" coating type approximately 3.5% of NCO in the prepolymer) Example l,4-diamino solution viscosity solution m-value cyclohexane cis/ poises/C concentration trans content Example Ultimate Breaking HDT determined melting behavior solvent tensile elongation in accordance with Kofler bench g/dtex 7: DOS 1,770,591 softening melting point 'C C (liquid) "C 3 a) 0.69 487 150 "Skies- 235 236' so'ivesso iooierh l'erie glycol (l l) 3 b) 0.64 450 69 from 152 203 Solvesso-lOO/ethylene glycol (l l) 0.66 450 106 from 178 2l4 Solvesso-lOO/ethylene glycol (l l) 4 0,74 525 I18 222-235 260 toluene/isopropanol 5 0.82 436 117 220 260 toluene/isopropanol 6 0,-68 464 l54 240 260 toluene/isopropanol (prepolymer: 5.44% NCO finish type) EXAMPLE 7 which comprises, reacting in an inert organic solvent a NCOPrePOWmer formation 25 a. chain extender comprising at least 80 mol 1,4-

1300 parts of the hexane diol polycarbonate described in Example 1 and 145 parts of the mixed polyester of Example 4 are reacted at around 980C with 339 parts of l-isocyanato-3-isocyanato methyl-3,5,5 trimethyl cyclohexane and 446 parts of toluene to form an NCO-prepolymer with an NCO-content of 3.60% (based on solid substance).

Reaction with diamino cyclohexane in perchlorethylene/isopropanol as solvent 8.48 parts of diamino cyclohexane (36/64 cis/trans) are dissolved in a 1 1 mixture of perchlorethylene and isopropanol (570 parts) and the resulting solution stirred with 205 parts of the above prepolymer solution until the viscosity of the approximately 22% solution has risen to 340 poises. The excess terminal amino groups are removed by the addition of approximately 0.7 parts of butyl isocyanate.

Reaction in trichlorethylene/isopropanol as solvent 4.24 parts of diamino cyclohexane (34/64'cis/trans) are dissolved in .207 parts of trichlorethylene and 89 parts of isopropanol and the resulting solution stirred with 107.5 parts of the above NCO-prepolymer solution to form a homogeneous, clear solution with a viscosity of 293 poises: c 22%.

Clear, highly elastic films are obtained from the elastomer solutions, giving a soft tack-free feel after lamination on to cotton fabric. The coatings are extremely resistant to hydrolysis.

It is to be understood that any of the components and conditions mentioned as suitable herein can be substituted for its counterpart in the foregoing examples and that although the-invention has been described in considerable detail in the foregoing, such detail is solely for the purpose of illustration. Variations can be made in the invention by those skilled in the art without departing from the spirit and scope of the invention except as is set forth in the claims.

What is claimed is:

l. polyur ethar e polyurea prepared by a process diamino cyclohexane with a cis/transisomer ratio of from 10/90 to /40, with b. an isocyanato terminated prepolymer prepared by a process which comprises reacting i. substantially linear polyhydroxyl compounds with molecular weights of from 500 to 5000, with ii. aliphatic or cycloaliphatic diisocyanates, the molar ratio of hydroxyl groups to isocyanate groups being between about 1 1.5 and l 5, and evaporating the solvent.

2..The product of claim 1 wherein the solvent used is a mixture of an aromatic hydrocarbon, or chlorinated aliphatic hydrocarbon, with primary secondary or tertiary aliphatic alcohols.

3. A product according to claim 1 wherein the isocyanato terminated prepolymers are prepared from substantially linear polyhydroxyl compounds with molecular weights of from about 62 to 400.

4. The product of claim 1 wherein the prepolymers, diamines and chain extenders are reacted in a solvent mixture of chlorinated aromatic hydrocarbons.

5. The product of claim 1 wherein the polyhydroxyl compounds are dihydroxy polyesters, polycarbonates or polyacetones.

6. The product of claim 1 wherein the prepolymer includes diols with a tertiary amino group.

7. The product of claim 1 wherein the diisocyanate mixture contains at least mol of l-isocyanato-3- eemate W l})f ';5t -Fi"1thll, yslqhexane.

8. The product of claim 1 wherein the molar ratio of isocyanate groups to amine groups in the chain extending reaction is between 1 1.0 and I 1.15.

9. The product of claim 1 wherein polyhydroxyl compound has a molecular weight of from 800 to 3000 and .a melting point below 45C by the Kofler Bench method. V. t 10. The product of claim 1 wherein the prepolymer includes a dihydroxy polyester selected from the group adipic acid-ethylene glycol, -l,6-hexanc diol, -2,2- dimethyl propane diol, -l,4-butane diol or -l,2- propane diol. 

1. A POLYURETHANE POLYUREA PREPARED BY A PROCESS WHICH COMPRISES, REACTING IN AN INERT ORGANIC SOLVENT A A. CHAIN EXTENDER COMPRISING AT LEAST 80 MOL % 1,4-DIAMINO CYCLOHEXANE WITH A CIS/TRANSISOMER RATIO OF FROM 10/90 TO 60/40, WITH B. AN ISOCYANTO TERMINATED PREPOLYMER PREPARED BY A PROCESS WHICH COMPRISES REACTING I. SUBSTANTIALLY LINEAR POLYHYDROXY COMPOUNDS WITH MOLECULAR WEIGHTS OF FROM 500 TO 5000, WITH II. ALIPHATIC OR CYCLOALIPHTIC DIISOCYANATE THE MOLAR RATIO OF HYDROXY GROUPS TO ISOCYANATE GROUPS BEING BETWEEN ABOUT 1:1.5 AND 1: 5, AND EVAPORATING THE SOLVENT.
 2. The product of claim 1 wherein the solvent used is a mixture of an aromatic hydrocarbon, or chlorinated aliphatic hydrocarbon, with primary secondary or tertiary aliphatic alcohols.
 3. A product according to claim 1 wherein the isocyanato terminated prepolymers are prepared from substantially linear polyhydroxyl compounds with molecular weights of from about 62 to
 400. 4. The product of claim 1 wherein the prepolymers, diamines and chain extenders are reacted in a solvent mixture of chlorinated aromatic hydrocarbons.
 5. The product of claim 1 wherein the polyhydroxyl compounds are dihydroxy polyesters, polycarbonates or polyacetones.
 6. The product of claim 1 wherein the prepolymer includes diols with a tertiary amino group.
 7. The product of claim 1 wherein the diisocyanate mixture contains at least 75 mol % of 1-isocyanato-3-isocyanato methyl-3, 5,5-trimethyl cyclohexane.
 8. The product of claim 1 wherein the molar ratio of isocyanate groups to amine groups in the chain extending reaction is between 1 : 1.0 and 1 : 1.15.
 9. The product of claim 1 wherein polyhydroxyl compound has a molecular weight of from 800 to 3000 and a melting point below 45*C by the Kofler Bench method.
 10. The product of claim 1 wherein the prepolymer includes a dihydroxy polyester selected from the group adipic acid-ethylene glycol, -1,6-hexane diol, -2,2-dimethyl propane diol, -1,4-butane diol or -1,2-propane diol. 